| 品牌 | 南通三菱麗陽 |
|---|---|
| 貨號 | PMMA IR K304 |
| 用途 | 工程應用 |
| 牌號 | PMMA IR K304 |
| 型號 | PMMA IR K304 |
| 品名 | PMMA |
| 外形尺寸 | 來電詢問 |
| 生產企業 | 南通三菱麗陽 |
| 是否進口 | 是 |
供應 PMMA IR K304南通三菱麗陽 紫外線穩定 沖擊改性
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17g/cc | 1.17g/cc | ISO 1183; JIS K7112 |
| Water Absorption | 0.30 %@Time 86400 sec | 0.30 %@Time 24.0 hour | ISO 62 |
| Linear Mold Shrinkage | 0.0030-0.0070cm/cm | 0.0030-0.0070in/in | MRC method |
| Melt Flow | 3.0g/10 min@Load 3.80 kg,Temperature 230 °C | 3.0g/10 min@Load 8.39 lb,Temperature 446 °F | ISO 1133 |
| Spiral Flow | 150cm@Thickness 2.00 mm,Temperature 250 °C | 59.1in@Thickness 0.0787 in,Temperature 482 °F | MRC method |
| 270cm@Thickness 2.00 mm,Temperature 250 °C | 106in@Thickness 0.0787 in,Temperature 482 °F | MRC method | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80 | 80 | ISO 2039 |
| Tensile Strength | 65.0MPa | 9430psi | 1A/5; ISO 527 |
| Elongation at Break | 19 % | 19 % | 1A/5; ISO 527 |
| Modulus of Elasticity | 2.30GPa | 334ksi | 1A/1; ISO 527 |
| Flexural Strength | 98.0MPa | 14200psi | ISO 178 |
PMMA原料的特性：
無色透明，透光率達90%---92%，韌性強，比硅玻璃大10倍以上。
光學性、絕緣性、加工性及耐候性佳。
溶解于四氯化碳、苯、甲苯二氯乙烷、三氯甲烷和丙酮等有機溶劑。
具有較高透明度和光亮度，耐熱性好，并有堅韌，質硬，剛性特點，熱變形溫度80℃，彎曲強度110Mpa。
密度1.14—1.20g/cc,變形溫度76--116℃，成型收縮率0.2—0.8%。
線膨脹系數0.00005—0.00009/℃,熱變形溫度68--69℃(74--107℃)
PMMA用途
PMMA具有質輕、價廉，易於成型等優點。溶于有機溶劑如苯甲醚等，可以形成良好的薄膜和良好的介電性能，可以作為有機場效應管的介質層。 [1]
它的成型方法有澆鑄，射出成型，機械加工、熱成型等。尤其是射出成型，可以大批量生產，制程簡單，成本低。因此，它的應用日趨廣泛，它廣泛用于儀器儀表零件、汽車車燈、光學鏡片、透明管道。
有機玻璃壓克力（亞克力）在建筑業中的應用在建筑方面，有機玻璃壓克力（亞克力）主要應用于建筑采光體、透明屋頂、棚頂、電話亭、樓梯和房間墻壁護板等方面；衛生潔具方面有浴缸、洗臉盆、化妝臺等產品。在高速公路及高等級道路照明燈罩及汽車燈具方面的應用發展也相當快。其中，建筑采光體、浴缸、街頭廣告燈箱和電話亭等方面的市場增長較快，今后的發展空間較大，市場前景十分廣闊。